Evaluation of cytotoxicity levels of poly vinyl ether silicone, polyether, and poly vinyl siloxane impression materials: An in vitro study
N Vivek Rajasimhan1, Srinivasan Jayaraman2, Doulathunnisa Jaffar Ali3, Balanehru Subramanian4
1 Department of Prosthodontics and Crown and Bridge, Tagore Dental College, Tamil Nadu Dr. MGR Medical University, Chennai, Tamil Nadu, India
2 Department of Prosthodontics, Faculty of Dentistry, Al Baha University, Al Baha, Saudi Arabia
3 Scientist-Biological and Molecular Science, State Key Laboratory of Bioelectronics, School of Biological Science and Medical Engineering, Southeast University, Nanjing, China
4 Director - Research, Central Inter-Disciplinary Research Facility, Center for Animal Research, Training and Services, MGMCRI Campus, Puducherry, India
|Date of Submission||16-Jul-2019|
|Date of Decision||29-Aug-2019|
|Date of Acceptance||15-Sep-2019|
|Date of Web Publication||10-Oct-2019|
Dr. N Vivek Rajasimhan
Department of Prosthodontics and Crown and Bridge, Tagore Dental College, Tamil Nadu Dr. MGR Medical University, Chennai, Tamil Nadu
Source of Support: None, Conflict of Interest: None
Aim: To assess the cytotoxicity level of newly introduced poly vinyl ether silicone (PVES) compared to poly vinyl siloxane (PVS) and polyether (PE) elastomeric impression materials.
Settings and Design: Comparative -Invitro study design.
Materials and Methods: Mouse cell line NIH/3T3 was grown in Dulbecco's modified Eagle's medium. Samples of three elastomers were dissolved in dimethyl sulfoxide and were tested at various concentrations. Twenty-four well plates with NIH/3T3 cells with different concentrations of elastomeric solutions were incubated at 37°C. 3-(4,5-dimethylthiazol-2-yl)-2-5-diphenyltetrazolium bromide assay was performed on day 1, 3, and 7, with a time interval of 15 min, 30 min, 60 min, and 24th h to estimate the cytotoxicity for all three elastomers.
Statistical Analysis Used: Kruskal–Wallis ANOVA test and the period effect within the subjects, repeated-measure ANOVA was done using the Greenhouse–Geisser correction method.
Results: The mean cell viability (survival rate) of NIH 3T3 cells at the concentrations tested was measured. A repeated-measure Kruskal–Wallis ANOVA determined the mean survival concentration on day 1, 3, and 7. PVES showed significant decrease in the survival rate on day 1 than PVS and PE, while PVS and PE had significant decrease in the survival rates of cells on day 3 and 7 which were statistically significant (P < 0.001).
Conclusion: PVES shows early cytotoxic signs as compared to PVS and PE, and cell viability for PVS was the highest among all. When making impression with PVES and PE, it is always better to evaluate the impression and gingival sulcus carefully with magnification to prevent adverse reaction, if any material is left inadvertently for longer period of time.
Keywords: 3-(4,5-dimethylthiazol-2-yl)-2-5-diphenyltetrazolium bromide assay, biocompatibility, cell viability, cytotoxicity, mouse cell lines
|How to cite this article:|
Rajasimhan N V, Jayaraman S, Ali DJ, Subramanian B. Evaluation of cytotoxicity levels of poly vinyl ether silicone, polyether, and poly vinyl siloxane impression materials: An in vitro study. J Indian Prosthodont Soc 2019;19:332-7
|How to cite this URL:|
Rajasimhan N V, Jayaraman S, Ali DJ, Subramanian B. Evaluation of cytotoxicity levels of poly vinyl ether silicone, polyether, and poly vinyl siloxane impression materials: An in vitro study. J Indian Prosthodont Soc [serial online] 2019 [cited 2021 Jan 22];19:332-7. Available from: https://www.j-ips.org/text.asp?2019/19/4/332/268769
| Introduction|| |
Final impression materials used in fixed, removable, and implant prosthodontics are elastomers. The newly introduced poly vinyl ether silicone (PVES) elastomer claims combined advantage of dimensional accuracy of poly vinyl siloxane (PVS) and hydrophilic nature of polyether (PE).,,, Multiple adverse reactions have been reported on PE than additional silicone, and it can range from mild irritation to delayed hypersensitivity reaction happening after 24 h to 1–3 days., The clinical manifestation includes severe pain, dry mouth, burning mouth, swelling of lips, nonspecific cheilitis, dermatitis, and dysphagia.,
The elastomers can tear and can be trapped in the gingival sulcus under implants during impression making and cause adverse and toxic reactions when remained in contact for longer periods of time.,,,,,,,,,,,,,,, There are many reports on cytotoxicity, tissue reactions, and hypersensitivity of various other dental materials.,, The potential cytotoxicity of these materials can be tested either by introducing the cells into the material (direct test) or to the eluted extracts of the impression materials (indirect tests). The assessment of cytotoxicity of these materials is a fundamental step in the evaluation of their biocompatibility. PVES combines the advantages of PVS and PE. No independentin vitro study has been reported in the literature on the cytotoxic levels of PVES compared to PVS and PE at the time of start of the study. The aim of this study is to evaluate cytotoxicity of PVES impression material compared to PVS and PE impression materials on NIH/3T3 cells (mouse cell line) cultured in vitro. The objective is to evaluate the cytotoxicity level of PVES, PE, and PVS on NIH/3T3 cell for cell viability on day 1, 3, and 7 with a time interval of 15 min, 30 min, 60 min, and 24th h. Null hypothesis means no difference between the PVES, PVS, and PE material in cytotoxicity levels over the three time points on day 1, 3, and 7.
| Materials and Methods|| |
The study was approved by the Institutional Review Board (IRB Approval No.: IGIDSIRB2014 NRP14PGVRPCI). Elastomeric impression materials used were light body, soft consistency supplied in paste forms: Group A – PVES (EXA'lence light body, GC America, LOT No.: 1306121, expiry: 2. December 2015); Group B – PVS (Flexceed light body, GC America, LOT No.: 1401031, expiry: January 2017); and Group C – PE impression material (Impregum Soft Consistency, hand mix, hydrophilic, 3M ESPE, Germany, LOT No.: 31710, expiry: March 2017).
Cells were cultured using Dulbecco's modified Eagle's medium (DMEM), 4.5 g glucose/l, L-glutamine and sodium pyruvate, fetal bovine serum (FBS), and 1X phosphate-buffered saline (PBS) (HiMedia Labs, Mumbai, India). Thiazolyl blue tetrazolium bromide 98% (Sigma, Biocorporals, Chennai, India, Cat No.: M2128100MG) and trypsin 0.25% ethylenediaminetetraacetic acid, phenol red (Gibco, Biocorporals, Chennai, India, Cat No.: 25200056 – 100 ml). The cytotoxic tests were carried out on day 1, 3, and 7, with the time interval of 15 min, 30 min, 60 min, and 24th h.
Specimen preparation was done following the International Organization for Standardization standards for cell cytotoxic study., The impression materials [Figure 1] were dispensed and mixed individually according to the manufacturer's instructions and placed in a sterilized brass mold of size 1 cm × 1 cm; after polymerization, the specimen was stored in a glass container. A total of eight specimens were made for each impression material. All the prepared samples [Figure 2] were handled in aseptic conditions to avoid biologic contamination during cell culture tests.
|Figure 2: Prepared samples purple polyether, pink poly vinyl ether silicone, yellow poly vinyl siloxane|
Click here to view
The mouse fibroblast cell line NIH/3T3 was obtained from the National Centre for Cell Sciences, Pune. Cells were grown in DMEM, supplemented with 10% FBS, 2 mM-glutamine, 100 μg/ml streptomycin, and 100 U/ml of penicillin. The cells were maintained at 37°C in the incubator with 5% carbon dioxide (CO2). After few passages, on reaching 85% confluence, cells were washed with 1X PBS and seeded for further cytotoxicity assay.
Indirect cytotoxic testing methods were carried out in this study, [Figure 3]. NIH/3T3 cells were incubated with polymerized impression materials in 60-mm Petri dishes in 5 ml of culture medium without serum for 15 min, 30 min, 60 min, and 24th h at 37°C under sterile conditions [Figure 3]. The use of culture medium without serum was adopted to avoid the possible interaction or inactivation of substances released by testing materials with serum components. After incubation period, the culture medium containing any soluble extracts of polymerized impression materials was collected in sterile tubes and used for further testing.
3-(4,5-dimethylthiazol-2-yl)-2- 5-diphenyltetrazolium bromide assay
3-(4,5-dimethylthiazol-2-yl)-2-5-diphenyltetrazolium bromide (MTT) assay is one of the most commonly used calorimetric assays to assess cytotoxicity or cell viability. This assay determines principally cell viability through determination of mitochondrial function of the cells by measuring activity of mitochondrial enzymes, such as succinate dehydrogenase. This method is far superior to the previously mentioned dye exclusion methods because it is easy to use and safe, has a high reproducibility, and is widely used to determine both cell viability and cytotoxicity tests.,
NIH/3T3 cells were seeded in a 96-well plate at a density of 5 × 103 cells/well with complete DMEM supplemented with 10% FBS [Figure 4]. After 24 h, the used medium was removed and the cells were washed with 1X PBS. Cells were exposed to 100 μl of extracts for day 1, 3, and 7, with the time interval of 15 min, 30 min, 60 min, and 24th h; the time interval is used to differentiate the level of survival percentage of cells and cytotoxic virulence between each time interval. The same time interval is followed for day 3 and 7. 50 μl of MTT (5 mg/ml in PBS) was added to each well. Subsequently, the plates were incubated at 37°C for 3 h at 5% CO2. At end of the incubation, excess MTT solution was removed and the formazan crystals were dissolved with 100 μl of dimethyl sulfoxide. Finally, the color intensity was measured at 570 nm in SpectoMax M5, Molecular Devices, CA, USA.
|Figure 4: 3-(4, 5-dimethylthiazol-2-yl)-2-5-diphenyltetrazolium bromide assay|
Click here to view
Continuous data will be reported as mean and standard deviation and dichotomous data as percentages. Data will be checked for normality to use parametric or nonparametric test. To estimate the difference in the primary outcome ANOVA test or Kruskal–Wallis ANOVA test 4 will be used to check, cell viability (survival rate of cells) at various time point on day 1, 3, and 7. To assess the period effect, ANOVA test, using Greenhouse–Geisser method, will be used to test the cell viability changes over time in each group. The alpha error was set to 0.05 to determine the statistical significance.
| Results|| |
The amount of cell viability (survival rate) of the NIH 3T3 cells on each day of measurement at various time points (15 min, 30 min, 60 min, 24th h) for each material independently, from the eluates obtained from PVES, PVS, and PE, is presented in [Table 1]. The nonparametric method Kruskal–Wallis ANOVA test is used to measure mean and standard deviation of cell viability (survival rate of cells) of the NIH 3T3 on day 1, 3, and 7 for the eluates obtained from PVES, PVS, and PE [Table 2]. Statistically significant difference was observed at each day (P < 0.001). To assess the period effect within the subjects, repeated-measure ANOVA was done using the Greenhouse–Geisser correction method and the results are presented in [Table 3]. Pairwise comparison of each day is reported in [Table 4], [Table 5], [Table 6].
|Table 1: Cell viability (survival of cells at different time point in a single day of measurement)|
Click here to view
|Table 2: Mean survival rate (average cell viability survival of cells on each day)|
Click here to view
| Discussion|| |
The study rejects the null hypothesis of no difference between the PVES, PVS, and PE material in cytotoxicity levels over the three time points on day 1, 3, and 7. The mean survival rate (cell viability) at day 1 for PVES was very low mean (25.55) compared to PE (107.5) and PVS (119.75) with P < 0.001 being statistically significant. At day 3 and 7, PVES (22.13 and 23.6) materials' cell viability unchanged for PE (65.5 and 17.7) and PVS (92.5 and 72.04) with P < 0.001. These results inferred that there will be early inflammatory signs with PVES compared PE and PVS; hence, PVS and PE should not be inadvertently left in the gingival sulcus after impression making. To assess the period effect in all three groups, PVES was not statistically significant as there was no change from day 1 to 7, but PE and PVS were statistically significant (P < 0.05). Cell viability for PVS was the highest among all. Pairwise comparison for survival of the impression material confirms that PE and PVS have more survival rate at day 1, 3, and 7 than PVES. Significant differences were found on day 1 and 7 for PE and PVS, whereas no significant differences were found for any of the days in PVES, which denotes that the incidence of cytotoxic effects will be earlier in case of PVES compared to that of PE and PVS.
Boraldi et al. and Roberta et al. assessed the cell viability after 12 h, 24 h, and maximum of 48 h., In the current study, the cell viability is tested after 24 h, 3 days, and 7 days, which will substantiate that both early and delayed cytotoxic signs can be assessed, as in case if impression material is inadvertently left in the gingival sulcus for longer period of 7 days. Studies done by Blankenau et al., Rafael and Liebermann, Batchelor and Todd, Mittermüller et al., Roberta et al., Nally and Storrs, Brunton et al., and Smith andWilliams concluded that there is allergic response, contact dermatitis, and gingivitis and may provoke hypersensitive reactions to PE impression material.,,,,,,, Roberta et al. also concluded that PE is more cytotoxic than PVS, which matches with the results of our study. In the current study, along with PE and PVS, PVES is also assessed for cytotoxicity and no study has compared till date. The adverse reactions of these impression materials occur when entrapped material remains within the gingival sulcus, under the suture, within the soft tissues, periosteum, and maxillary sinus; when an impression is made, careful inspection of the gingival sulcus and impression for after removal with magnification is requited to prevent adverse reactions.,,,
There are limitations for the current study, as it is anin vitro study with mouse cell line and not gingival fibroblast or immortalized human oral fibroblasts. A study done by Sung Kwon and Nam Kim in 2014 stated that selecting the cells lines for the cytotoxic study of impression material is important for interpreting the results for cytotoxic evaluation; using human-based cell lines like hTERT-hNOF (immortalized human oral fibroblasts) would be appropriate for both ease of cytotoxicity test and more accurate clinical relevance. Further,in vivo research is needed to confirm the results of this study.
| Conclusion|| |
PVES shows early cytotoxic signs as compared to PVS and PE. Cell viability for PVS was the highest among all at day 7. When making impression with PE and PVES, it is always better to evaluate the impression and gingival sulcus carefully with magnification to prevent adverse reaction if any material is left inadvertently for longer period of time.
Financial support and sponsorship
Conflicts of interest
There are no conflicts of interest.
| References|| |
Rosenstiel SF, Land MF, Fujimoto J. Contemporary Fixed Prosthodontics. 4th
ed. St. Louis: Mosby Elsevier; 2006.
Sakaguchi R, Powers J. Craigs Restorative Dental Materials. 13th
ed. St. Louis: Elsevier; 2012.
Eames WB, Wallace SW, Suway NB, Rogers LB. Accuracy and dimensional stability of elastomeric impression materials. J Prosthet Dent 1979;42:159-62.
Ciesco JN, Malone WF, Sandrik JL, Mazur B. Comparison of elastomeric impression materials used in fixed prosthodontics. J Prosthet Dent 1981;45:89-94.
Nassar U, Oko A, Adeeb S, El-Rich M, Flores-Mir C. Anin vitro
study on the dimensional stability of a vinyl polyether silicone impression material over a prolonged storage period. J Prosthet Dent 2013;109:172-8.
Blankenau RJ, Kelsey WP, Cavel WT. A possible allergic response to polyether impression material: A case report. J Am Dent Assoc 1984;108:609-10.
Rafael CF, Liebermann A. Clinical characteristics of an allergic reaction to a polyether dental impression material. J Prosthet Dent 2017;117:470-2.
Batchelor JM, Todd PM. Allergic contact stomatitis caused by a polyether dental impression material. Contact Dermatitis 2010;63:296-7.
Mittermüller P, Szeimies RM, Landthaler M, Schmalz G. A rare allergy to a polyether dental impression material. Clin Oral Investig 2012;16:1111-6.
Roberta T, Federico M, Federica B, Antonietta CM, Sergio B, Ugo C. Study of the potential cytotoxicity of dental impression materials. Toxicol In Vitro
Kwon JS, Lee SB, Kim CK, Kim KN. Modified cytotoxicity evaluation of elastomeric impression materials while polymerizing with reduced exposure time. Acta Odontol Scand 2012;70:597-602.
Boraldi F, Coppi C, Bortolini S, Consolo U, Tiozzo R. Cytotoxic evaluation of elastomeric dental impression materials on a permanent mouse cell line and on a primary human gingival fibroblast culture. Materials (Basel) 2009;2:934-44.
Marshak BL, Cardash HS, Ben-Ur Z. Incidence of impression material found in the gingival sulcus after impression procedure for fixed partial dentures. J Prosthet Dent 1987;57:306-8.
Al-Hiyasat AS, Darmani H, Bashabsheh OM. Cytotoxicity of dental casting alloys after conditioning in distilled water. Int J Prosthodont 2003;16:597-601.
Coppi C, Paolinelli Devincenzi C, Bortolini S, Consolo U, Tiozzo R. A new generation of sterile and radiopaque impression materials: Anin vitro
cytotoxicity study. J Biomater Appl 2007;22:83-95.
Jeng HW, Feigal RJ, Messer HH. Comparison of the cytotoxicity of formocresol, formaldehyde, cresol, and glutaraldehyde using human pulp fibroblast cultures. Pediatr Dent 1987;9:295-300.
Ozen J, Sipahi C, Caglar A, Dalkiz M.In vitro
cytotoxicity of glass and carbon fiber-reinforced heat-polymerized acrylic resin denture base material. Turk J Mes Sci 2006;36:121-6.
Liu CM, Huang FM, Yang LC, Chou LS, Chou MY, Chang YC, et al
. Cytotoxic effects of gingival retraction cords on human gingival fibroblasts in vitro
. J Oral Rehabil 2004;31:368-72.
Sabaliauskas V, Juciute R, Bukelskiene V, Rutkunas V, Trumpaite-Vanagiene R, Puriene A.In vitro
evaluation of cytotoxicity of permanent prosthetic materials. Stomatologija 2011;13:75-80.
Yousef H, Sharbeh A, Ponnuraj T, Raja RA.In vitro
cytotoxicity evaluation porcelain using human cell lines of dental. Arch Orafac Sci 2012;7:68-74.
Chen SY, Chen CC, Kuo HW. Cytotoxicity of dental impression materials. Bull Environ Contam Toxicol 2002;69:350-5.
Al Mobeeriek A, Al-Elshiekh H. Adverse effect of polysulfide impression material case report. Saudi Dent J 1998;10:86-8.
Nally FF, Storrs J. Hypersensitivity to a dental impression material. A case report. Br Dent J 1973;134:244-6.
van Groeningen G, Nater JP. Reactions to dental impression materials. Contact Dermatitis 1975;1:373-6.
Dahl BL. Tissue hypersensitivity to dental materials. J Oral Rehabil 1978;5:117-20.
Reddy NR, Abraham AP, Murugesan K, Matsa V. Anin vitro
analysis of elemental release and cytotoxicity of recast nickel-chromium dental casting alloys. J Indian Prosthodont Soc 2011;11:106-12.
Chandar S, Kotian R, Madhyastha P, Kabekkodu SP, Rao P.In vitro
evaluation of cytotoxicity and corrosion behavior of commercially pure titanium and ti-6Al-4V alloy for dental implants. J Indian Prosthodont Soc 2017;17:35-40.
] [Full text]
Jagdish SK, Ganeshkumar A, Shakila R, Singh S, Jesudas B, Karthikeyan S. Effect of isobutyl methacrylate and methacrylic acid eluted from chairside denture hard reliners on enzymatic cellular antioxidants: Anin vitro
study in human primary buccal mucosal fibroblasts. J Indian Prosthodont Soc 2017;17:189-95.
] [Full text]
Mosmann T. Rapid colorimetric assay for cellular growth and survival: Application to proliferation and cytotoxicity assays. J Immunol Methods 1983;65:55-63.
Stone V, Johnston H, Schins RP. Development ofin vitro
systems for nanotoxicology: Methodological considerations. Crit Rev Toxicol 2009;39:613-26.
Aslanturk OS, Askın Celik T, Karabey B, Karabey F. Active phytochemical detecting, antioxidant, cytotoxic, apoptotic activities of ethyl acetate and methanol extracts of Gallium aparine L. Br J Pharma Res 2017;15:1-16.
Brunton PA, Christensen GJ, Cheung SW, Burke FJ, Wilson NH. Contemporary dental practice in the UK: Indirect restorations and fixed prosthodontics. Br Dent J 2005;198:99-103.
Smith DC, Williams DF. Composition, characteristics and clinical and tissue reactions of impression materials. Biocompatibility of Dental Materials. Vol. 3. Boca Raton, FL, USA: CRC Press; 1982. p. 277-89.
Shiloah J, Schuman NJ, Covington JS, Turner JE. Periodontal hazards of retained impression materials. Quintessence Int 1988;19:143-7.
Gullett CE, Caulder SL. Residual fragment of rubber base material. Oper Dent 1978;3:131-2.
Price C, Whitehead FI. Impression materials as foreign bodies. Br Dent J 1972;133:9-14.
Winstock D, Warnakulasuriya S. Impression material presenting in the maxillary antrum as a foreign body. Br Dent J 1986;160:54-5.
Sung Kwon J, Nam Kim K. Cytotoxicity evaluation of elastomeric impression materials using different fibroblasts cell lines. J Korean Dent Sci 2014;7:80-6.
[Figure 1], [Figure 2], [Figure 3], [Figure 4]
[Table 1], [Table 2], [Table 3], [Table 4], [Table 5], [Table 6]